Ytterbium is a lustrous silver metal, and very malleable.  Ytterbium is of the rare earth family of elements and is reported to be the easiest of the rare earths to be rolled into thin sheets. Ytterbium, is formed by neutron irradiation of thullium. It is used as a portable radiograh source and foils are used to measure pressure and stress transducers. In it’s beta form, it is semiconductive at pressures above 16,000 atmospheres. One of ytterbium’s isotopes (170Yb) is used as a portable x-ray source. Ytterbium is also used in lasers, phosphors, ceramic capacitors, ferrite devices, catalysts and as a dopant for garnets.

General Characteristics:

Atomic Weight: 173.04

Hardness: 17 HV

Poisson’s Ratio: 0.207

Strain-Hardening Exponent: 0.62


α phase, 6.903 g/cm3 at 23 oC

β phase, 6.966 g/cm3 at 24 oC

γ phase, 6.57 g/cm3 at 763 oC

Crystal Structure:

α phase: close-packed hexagonal, P63/mmc Dh4; a=0.38799nm, c=0.63859nm at 24oC.

β phase: face-centered cubic, Fm3m Oh5; a=0.54848 nm at 24 oC

γ phase: body-centered cubic, Im3m Oh9, a=0.444 nm at 763 oC

        Thermal Properties:

Melting Point: 824 oC

Boiling Point: 1196 oC

Phase Transformation Temperature:

α to β phase: As = 280 K

β to α phase: Ms ≅ 260 K

β to γ phase: 795 oC

Coefficient of Thermal Expansion (24oC):

Linear: 26.3 μm/m ⋅ K

Linear along crystal axes: 26.3 μm/m ⋅ K along a axis

Volumetric: 78.9 x 10-6 per K

Recrystallization Temperature: Approximately 300 oC

Thermal Conductivity: 38.5 W/m ⋅ K at 25 oC

Vapor Pressure:  

     301 oC: 0.001 Pa

     400 oC: 0.101 Pa

     776 oC:  1013 Pa

       Electrical Properties:

Electrical Resistivity: 250 nΩ ⋅ m at 25 oC; 10 nΩ ⋅ m at 4 K

Temperature of Superconductivity: Bulk ytterbium is not superconducting down to 0.015 K at atmospheric pressure.

Magnetic Susceptibility: Volume: 3.4 x 10-6 mks at 17 oC

Thermal Neutron Cross Section: 37 b

       Corrosion Properties:

General Behavior: Ytterbium tarnishes slightly in moist air. It oxidizes slowly at elevated temperatures and reacts readily with hydrogen at 250 oC.

Resistance to Specific Corroding Agents: Ytterbium does not react with cold water, but it will tarnish in hot water. It reacts vigorously with dilute acids.

       Chemical Properties:

Ytterbium does not react with cold waer but will tarnishes in hot water and slightly in moist air. It oxidizes slowly at elevated temperatures and reacts readily with hydrogen at 250o C.

       Mechancial Properties:

Tensile Properties (Room Temperature):

Tensile strength: 58 MPa

Yield strength: 7 MPa

Elongation: 43%

Reduction in area: 92%

Elastic Modulus (27 oC) 

Tension: 23.9 GPa

Shear:   9.9 GPa

Bulk: 30.5 GPa

Kinematic Liquid Viscosity: 0.430 mm2/s at 824 oC

Liquid Surface Tension: 0.320 N/m at 820 oC


Home Page Content Under Periodic Table


Click on the Alloy to go to the Online Catalog page.


Welcome to

ESPI was incorporated in 1950 with a mission to provide a competitive source for high purity metals, metal compounds and alloys. We are a valuable resource for virtually all major universities worldwide, global corporate R&D laboratories, thousands of domestic and international manufacturing companies and all U.S. government research laboratories. ESPI offers unique advantages often unavailable from larger organizations with no minimum order size & all business hour calls are handled by a competent sales representative. Automated answering systems and voice mail are not an option at ESPI.

Located within our fabrication facility is the melting department, forging & shaping areas, and the rod & wire, and sheet & foil departments providing the following manufacturing capabilities:

  • Casting of pure metals and alloys
  • Vacuum arc melting
  • Induction melting
  • Rod and wire drawing/extrusion
  • Sheet, foil and ribbon rolling
  • CNC milling and machining

Tel: 541-488-8311 - Email: - or click the "Live Help/Chat Now" icon, upper right.



ESPI produces and sells 68 elements and dozens of alloys in various forms for your custom needs. Click on the forms below to be directed to detailed information on manufacturing.



At We Keep Good Company

Aerospace and Defense
Northrop Grumman, Hewlett Packard, IBM, Lockheed-Martin, Hughes, Boeing, General Dynamics, Aerojet, Litton, General Electric

Medical Instruments & Technology
Cintron, Hologic/Lorad, Varian, Siemens Medical, St Jude Medical, ArthroCare, GE Medical, Harvard Medical School, City of Hope Medical Center, American Medical Systems, Cedars Sinai Medical Center

Atomic Energy of Canada, CNRS, European Synchrotron Radiation Facility, INRS, Alberta Research Council, National Research Council of Canada, UNAM, CISRO, CERN

Stanford, UCLA, Harvard, Georgia Institute of Technology, Caltech, Johns Hopkins University, University of Arizonia, Penn State, University of Michigan, Princeton, Yale, University of Wollongong, University of Tokoyo, University of Toronto, Tulane, University of New South Wales, Max-Planck Institute, University of Freiburg

Government Research Labs
JPL, Los Alamos National Lab, Battelle Pacific NW National Lab, US Department of Energy, Argonne National Lab, Brookhaven National Lab, Naval Oceans Systems Center, US Air Force, Lawrence Berkeley National Lab, NASA

Green Energy
Origin Energy Solar, First Solar, Schott Solar, SunPower Corporation, Nanosolar, Inc.